[vc_empty_space][vc_empty_space]
Synthesis of uniformly porous NiO/ZrO2 particles
Balgis R.a, Iskandar F.a,b, Ogi T.c, Purwanto A.d, Okuyama K.a
a Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, Japan
b Department of Physics, Bandung Institute of Technology, Indonesia
c Department of Chemical Engineering, Osaka Prefecture University, Japan
d Department of Chemical Engineering, Sebelas Maret University, Indonesia
[vc_row][vc_column][vc_row_inner][vc_column_inner][vc_separator css=”.vc_custom_1624529070653{padding-top: 30px !important;padding-bottom: 30px !important;}”][/vc_column_inner][/vc_row_inner][vc_row_inner layout=”boxed”][vc_column_inner width=”3/4″ css=”.vc_custom_1624695412187{border-right-width: 1px !important;border-right-color: #dddddd !important;border-right-style: solid !important;border-radius: 1px !important;}”][vc_empty_space][megatron_heading title=”Abstract” size=”size-sm” text_align=”text-left”][vc_column_text]Porous NiO-ZrO2 particles were successfully synthesized using a spray-drying method with polystyrene latex (PSL: 400 nm) as a template and starting materials that included NiO powder (7 nm) and ZrO2 sol (1.2 nm). Porous particles with an average diameter of 4.5 μm and nearly spherical, narrow pores with an average size of ∼300 nm were obtained from the precursor at a pH of 3.7. The Brunauer, Emmett and Teller (BET) surface area of the prepared particles was relatively high – about 27 m2/g. When the solution pH was increased to 9.7, the particle morphology became completely spherical, indicating that the morphology of prepared particles can be controlled by adjusting the pH. Calcinations at 900 and 1200 °C were carried out to estimate the thermal stability of the prepared particles, which had shrinkage of less than 36%. The existence of these pores means that various applications, such as electrodes and catalysts, will be possible for the prepared particles. © 2011 Elsevier Ltd. All rights reserved.[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Author keywords” size=”size-sm” text_align=”text-left”][vc_column_text]A. Composites,B. Chemical synthesis,C. Thermogravimetric analysis (TGA),C. X-ray diffraction,D. Surface properties[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Indexed keywords” size=”size-sm” text_align=”text-left”][vc_column_text]A. Composites,B. Chemical synthesis,C. Thermogravimetric analysis (TGA),C. X-ray diffraction,D. Surface properties[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Funding details” size=”size-sm” text_align=”text-left”][vc_column_text]The author would like to thank Ms. Nguyen Thie My Diep for assisting with the experimental work, and The Ministry of Education, Culture, Sports, Science and Technology (MEXT) of Japan for providing a doctoral scholarship for R.B.[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”DOI” size=”size-sm” text_align=”text-left”][vc_column_text]https://doi.org/10.1016/j.materresbull.2011.01.019[/vc_column_text][/vc_column_inner][vc_column_inner width=”1/4″][vc_column_text]Widget Plumx[/vc_column_text][/vc_column_inner][/vc_row_inner][/vc_column][/vc_row][vc_row][vc_column][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][/vc_column][/vc_row]