Interdiffusion of elements in aluminum 2024 clad during reheat treatment process at 495°c
Basuki E.a, Sutarnob, Samuelc
a Department of Metallurgical Engineering, Institute of Technology Bandung, Indonesia
b PT Dirgantara Indonesia, Indonesia
c BASF Corporation, Indonesia
[vc_row][vc_column][vc_row_inner][vc_column_inner][vc_separator css=”.vc_custom_1624529070653{padding-top: 30px !important;padding-bottom: 30px !important;}”][/vc_column_inner][/vc_row_inner][vc_row_inner layout=”boxed”][vc_column_inner width=”3/4″ css=”.vc_custom_1624695412187{border-right-width: 1px !important;border-right-color: #dddddd !important;border-right-style: solid !important;border-radius: 1px !important;}”][vc_empty_space][megatron_heading title=”Abstract” size=”size-sm” text_align=”text-left”][vc_column_text]Aluminum alloy 2024 is normally strengthened with alloying elements of Cu and Mg. As these elements reduce the corrosion resistance of the materials, a pure Al clad is normally applied. Nevertheless, during ageing at high temperatures, inter-diffusion between elements can occur causing the recession of the clad. This study investigated the inter-diffusion behavior of Al 2024 clad at ageing temperature of 495°C and predicted the clad lifetime due to reheat treatment process. The depletion rate of clad was found at 0.8 μm per-hour of heat treatment. It is predicted that the thickness of the Al 2024 clad will no longer meet with the specifications on heat treatment for 42 hours at 495°C. © (2014) Trans Tech Publications, Switzerland.[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Author keywords” size=”size-sm” text_align=”text-left”][vc_column_text]Ageing temperature,Al 2024,Alloy 2024,High temperature,Pure Al,Reheat treatment,Treatment process[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Indexed keywords” size=”size-sm” text_align=”text-left”][vc_column_text]Alloy 2024,Cladding,Depletion rate,Diffusion,Reheat treatment[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Funding details” size=”size-sm” text_align=”text-left”][vc_column_text][/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”DOI” size=”size-sm” text_align=”text-left”][vc_column_text]https://doi.org/10.4028/www.scientific.net/AMR.896.605[/vc_column_text][/vc_column_inner][vc_column_inner width=”1/4″][vc_column_text]Widget Plumx[/vc_column_text][/vc_column_inner][/vc_row_inner][/vc_column][/vc_row][vc_row][vc_column][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][/vc_column][/vc_row]