Analysis of compressive strength in flatwise and edgewise direction to characterize Al-7000 aluminium foam
Sutarnoa, Soepriyanto S.a, Korda A.A.a, Dirgantara T.a
a Department of Metallurgical Engineering-Faculty of Mining and Petroleum, Bandung Institute of Technology, Bandung, 40132, Indonesia
Abstract
© 2015 AIP Publishing LLC.The physical mechanical properties of Al-7000 aluminium foam product and processing has been evaluated in this study. The characterization through the compressive testing refers to flatwise direction provided more confident result than edgewise direction. This experiment may correlate with formation of side products of calcia alumina and alumina silica that involved in metal mixture of aluminium foam. These compounds are formed from additional calcium carbonate and silica in the mixture. Calcium carbonate (CaCO3) roles as a blowing agent source of carbon dioxide (CO2). The formation of calcia alumina (CaO.Al2O3) may role to strengthen of cell wall of aluminium foam and to improve the viscosity of melting metal. The Al-7000 aluminium foam indicated a decrease of compressive strength probably due to existence of alumina silica (3Al2O3.SiO2) in the metal mixture.
Author keywords
Indexed keywords
Aluminium foam,Compressive strength,Flatwise,Foam density