[vc_empty_space][vc_empty_space]
The effect of alkaline activator types on strength and microstructural properties of geopolymer from co-combustion residuals of bamboo and kaolin
Purbasari A.a,b, Samadhi T.W.a, Bindar Y.a
a Bandung Institute of Technology, Bandung, 40132, Indonesia
b Chemical Engineering Department, Diponegoro University, Semarang, 50275, Indonesia
[vc_row][vc_column][vc_row_inner][vc_column_inner][vc_separator css=”.vc_custom_1624529070653{padding-top: 30px !important;padding-bottom: 30px !important;}”][/vc_column_inner][/vc_row_inner][vc_row_inner layout=”boxed”][vc_column_inner width=”3/4″ css=”.vc_custom_1624695412187{border-right-width: 1px !important;border-right-color: #dddddd !important;border-right-style: solid !important;border-radius: 1px !important;}”][vc_empty_space][megatron_heading title=”Abstract” size=”size-sm” text_align=”text-left”][vc_column_text]© 2018, Gadjah Mada University. All rights reserved.Geopolymer as a Portland cement substitute had been synthesized from alkaline activation of co-combustion residuals of bamboo and kaolin. Types of used alkaline activators were NaOH solution, KOH solution, a mixture of NaOH solution-water glass, and a mixture of KOH solution-water glass. Geopolymer with NaOH solution as activator had a compressive strength which was higher compared to geopolymer with KOH solution as an activator. However, geopolymer with NaOH solution-water glass as activator had a compressive strength which was lower compared to geopolymer with KOH solution-water glass as activator either at room temperature curing or at a curing temperature of 60 °C. The use of water glass with NaOH or KOH solution as activator could increase the compressive strength of geopolymer and yielded geopolymer having denser and more homogeneous microstructure seen from SEM images. XRD patterns revealed the presence of sodium aluminosilicate hydrate in geopolymer with NaOH solution and NaOH solution-water glass as activators, and potassium aluminosilicate hydrate in geopolymer with KOH solution and KOH solution-water glass as activators. Furthermore, FTIR spectra indicated asymmetrical vibration of Si(Al)-O at around 1008 cm-1 related to geopolymer product.[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Author keywords” size=”size-sm” text_align=”text-left”][vc_column_text][/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Indexed keywords” size=”size-sm” text_align=”text-left”][vc_column_text]Alkaline activator,Bamboo,Cement,Geopolymer,Kaolin[/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”Funding details” size=”size-sm” text_align=”text-left”][vc_column_text][/vc_column_text][vc_empty_space][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][vc_empty_space][megatron_heading title=”DOI” size=”size-sm” text_align=”text-left”][vc_column_text]https://doi.org/10.22146/ijc.26534[/vc_column_text][/vc_column_inner][vc_column_inner width=”1/4″][vc_column_text]Widget Plumx[/vc_column_text][/vc_column_inner][/vc_row_inner][/vc_column][/vc_row][vc_row][vc_column][vc_separator css=”.vc_custom_1624528584150{padding-top: 25px !important;padding-bottom: 25px !important;}”][/vc_column][/vc_row]