Copyright © 2018 Barlian et al.Articular cartilage is an avascular tissue with limited regenerative property. Therefore, a defect or trauma in articular cartilage due to disease or accident can lead to progressive tissue deterioration. Cartilage tissue engineering, by replacing defective cartilage tissue, is a method for repairing such a problem. In this research, three main aspects-cell, biomaterial scaffold, and bioactive factors-that support tissue engineering study were optimized. Adipose-derived mesenchymal stem cells (ADSC) that become cartilage were grown in an optimized growth medium supplemented with either platelet rich plasma (PRP) or L-ascorbic acid (LAA). As the characterization result, the ADSC used in this experiment could be classified as Mesenchymal Stem Cell (MSC) based on multipotency analysis and cell surface marker analysis. The biomaterial scaffold was fabricated from the Bombyx morii cocoon using silk fibroin by salt leaching method and was engineered to form different sizes of pores to provide optimized support for cell adhesion and growth. Biocompatibility and cytotoxicity evaluation was done using MTT assay to optimize silk fibroin concentration and pore size. Characterized ADSC were grown on the optimized scaffold. LAA and PRP were chosen as bioactive factors to induce ADSC differentiation to become chondrocytes. The concentration optimization of LAA and PRP was analyzed by cell proliferation using MTT assay and chondrogenic differentiation by measuring glycosaminoglycan (GAG) using Alcian Blue at 605 nm wavelength. The optimum silk fibroin concentration, pore size, LAA concentration, and PRP concentration were used to grow and differentiate characterized ADSC for 7, 14, and 21 days. The cell morphology on the scaffold was analyzed using a scanning electron microscope (SEM). The result showed that the ADSC could adhere on plastic, express specific cell surface markers (CD73, CD90, and CD105), and could be differentiated into three types of mature cells. The silk fibroin scaffold made from 12% w/v concentration formed a 500 μm pore diameter (SEM analysis), and was shown by MTT assay to be biocompatible and to facilitate cell growth. The optimum concentrations of the bioactive factors LAA and PRP were 50 μg/mL and 10%, respectively. GAG analysis with Alcian Blue staining suggested that PRP induction medium and LAA induction medium on 12% w/v scaffold could effectively promote not only cell adhesion and cell proliferation but also chondrogenic differentiation of ADSC within 21 days of culture. Therefore, this study provides a new approach to articular tissue engineering with a combination of ADSC as cell source, LAA and PRP as bioactive factors, and silk fibroin as a biocompatible and biodegradable scaffold.

Bioactive factors,Biomaterial scaffold,Chondrogenesis,Osteoarthritis,Stem cells

https://doi.org/10.7717/peerj.5809